    题名: Evaluation of the Manufacturing and Functions of Complex Yarn and Fabrics
    作者: 林青玫;LIN, CHIN-MEI;林敬文;Lin, Ching-wen
    贡献者: 時尚設計學系
    日期: 2012-07
    上传时间: 2012-11-26 10:33:40 (UTC+8)
    摘要: In this research, bamboo charcoal/spandex (BC/S) complex yarn was fabricated using spandex as the core yarn, which was then wrapped with bamboo charcoal nylon textured yarn. The core yarn was first expanded and then wrapped with the wrapping yarn on a rotor twister machine at speeds of 4000, 6000, 8000, 10000, and 12000 r.p.m. The wrapping amount of the BC/S complex yarns were 2, 3, and 4 turns/cm. In order to evaluate the physical properties of the BC/S complex yarn, the maximum breaking strength, elongation, and elastic recovery rate were tested. We fabricated BC/S fabrics using circular knitting based on optimal manufacturing parameters. The BC/S complex yarn had an optimum elastic recovery
    rate of 98.89% when the rotor speed was 10000 r.p.m and the wrap number 4 turns/cm. The optimum tenacity of the yarn containing 44.0 dtex spandex was 4.22 cN/dtex when the rotor speed was 4000 r.p.m. and the wrap number 2 turns/cm. The anion density of the BC/S fabric increased with the wrap number; in particular, the fabric containing 76.9 dtex spandex displayed an optimum anion density of 54 anions/cc.
    關聯: FIBRES & TEXTILES IN EASTERN EUROPE,93(4):47-50.