English  |  正體中文  |  简体中文  |  Items with full text/Total items : 90074/105197 (86%)
Visitors : 7161403      Online Users : 114
RC Version 6.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://asiair.asia.edu.tw/ir/handle/310904400/17539


    Title: Evaluation of Recycled Far-infrared/Impact-Resistant Poly(propylene) Composite Plates
    Authors: 林敬文;Lin, Ching-wen;林青玫;LIN, CHIN-MEI
    Contributors: 時尚設計學系
    Date: 2010-08
    Issue Date: 2012-11-26 10:34:08 (UTC+8)
    Abstract: In this research, bamboo charcoal polyamide / polyurethane (BCP/PU) complex yarns and knitted fabrics were produced from bamboo charcoal polyamide textured yarn and polyurethane fibres. The polyurethane fibres were expanded and then wrapped with the bamboo charcoal polyamide textured yarn. Three manufacturing parameters were depicted as follows: the speeds of the rotor twister were 4000-12000 r.p.m., the wrapped counts of the BCP/PU complex yarns - 200 - 400 turns/m; and the expanded multiple of the polyurethane fibres was 3. Afterwards we fabricated BCP/PU complex knitted fabrics using a circular knitting machine. The tenacity of the BCP/PU complex yarns was 37258.4 cN/tex when the speed of the rotor twister was 4000 r.p.m. and the wrapped counts - 200 turns/m. Meanwhile, the elongation of the BCP/P complex yarns was 35.77% when the speed of the rotor twister was 4000 r.p.m. and the wrapped counts - 400 turns/m. The lower electric surface resistivity of the BCP/PU knitted fabrics was 3.33x10E10 (omega/Square) when the wrapped counts were 400 turns/m and the polyurethane fibres - 78 dtex. Moreover, when the wrapped counts were 200 turns/m, the optimum air permeability of the BCP/PU complex knitted fabrics with 44 dtex polyurethane fibres was 47.2 cm3/cm2/s, which was better than that with 78 dtex polyurethane fibres.
    Relation: Advanced Materials Research
    Appears in Collections:[時尚設計學系] 期刊論文

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML206View/Open


    All items in ASIAIR are protected by copyright, with all rights reserved.


    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback